ሉላዊ ከፍተኛ-ሙቀት ቅይጥ ዱቄት
ACME uses PREP method, which is using metal or alloy as the consumable electrode, and under the centrifugal force to produce spherical metal powder. This method avoid the slug and contact with refractory material, eliminate the non-metal impurities, and produce high purity spherical powder.
- ቴክኒካዊ ባህሪዎች
- ተዛማጅ አማራጭ ውቅር
ሉላዊ ከፍተኛ-ሙቀት ቅይጥ ዱቄት
ደረጃ | የኬሚካል ጥንቅር | የምርት ደረጃ | የንጥል መጠን ስርጭት | ||
ዋና አካል | Impurity Element | ብሔራዊ ደረጃ | የዩኤስ መደበኛ | ||
IN625 (GH3625) | Cr:20.0-23.0 Mo:8.0-10.0 Nb:3.15-4.15 Fe:≤5.0 Si:≤0.50 Ni:Bal | Ti:≤0.40 Al:≤0.40 ሲ፡≤0.10 Co:≤1.00 S :≤0.015 P :≤0.015 O :≤0.01 | GB / T14992-2005 | 15-45μm 15-53μm 53-120μm 53-150μm | |
IN718 (GH4169) | Ni:50.0-55.0 Cr:17.0-21.0 Nb:4.75-5.25 Mo:2.80-3.30 Ti:0.65-1.15 Al:0.20-0.80 Cu:≤0.30 Fe:Bal | O:≤0.01 | GB / T14992-2005 | 15-45μm 15-53μm 53-120μm 53-150μm | |
IN713C (ኬ 418) | Cr:11.5-13.5 Mo:3.8-4.8 Al:5.5-6.4 Ti:0.5-1.0 Nb:1.8-2.5 Ni:Bal | C :0.08-0.16 Fe:≤1.0 O :≤0.01 | GB / T14992-2005 | 15-45μm 15-53μm 53-120μm 53-150μm | |
IN939 | Cr:22.0-22.8 Co:18.5-19.5 W :1.8-2.2 Nb:0.9-1.1 Ta:1.3-1.5 Ti:3.6-3.8 Al:1.8-2.0 Zr:0.05-1.4 Ni:Bal | C :0.13-0.17 B :0.004-0.012 N :≤0.001 S :≤0.001 Pb:≤0.001 Bi:≤0.001 Ag:≤0.001 O :≤0.011 | GB / T14992-2005 | 15-45μm 15-53μm 53-120μm 53-150μm | |
K4648 | Cr:32.0-35.0 W :4.3-5.5 Mo:2.3-3.5 Al:0.7-1.3 Nb:0.7-1.3 Fe:≤0.5 C :0.03-0.1 | B :≤ 0.008 Ce:≤0.30 Si:≤0.30 S :≤0.01 Y :≤0.04 Ca:≤0.02 O :≤0.02 | GB / T14992-2005 | 15-45μm 15-53μm 53-120μm 53-150μm |